Experimental investigation on superplastic forming behavior of AA 6063/SiCp using stir casting

Abstract. Super pliancy is a reasonable method for framing complex-molded structures. The strategy has the
benefits of convey in uncommon formability and possibly giving great dimensional tolerance. Stir casting
method was effectively used to prepare the AA6063/ SiCp composite and followed by rolling process was
repeated until the sheet reduces to the required thickness of 2.5 mm. With the gas pressure forming the
composites were tested for superplastic forming. Instantaneous change in heights were measured through
LVDT (Linear Variable Differential Transformer). Gas pressure forming tests were conducted on various
percentages of SiCp composites. The biaxial superplastic forming tests were conducted at varioustemperatures between 520 ̊C to 600 ̊C and pressures between 0.2 MPa to 0.7 MPa. At the temperature of600 ̊C and 0.7 MPa the cracks were formed and the components were deformed.